Stainless Steel 904L Pipes Supplier. Stockholder And Exporter of Quality Stainless Steel 904L Pipes.

Stainless Steel 904L Pipes Specification, Chemical Compositions, Price List, Application, Stainless Steel 904L Pipes stockiest supplier & exporter.

317/317L Stainless Steel Pipes Product Range

Chemtech Alloys Stainless Steel India Exporters Stainless Steel 904L Seamless Pipes

Chemtech Alloys Stainless Steel India Exporters Stainless Steel 904L Welded Pipes

Chemtech Alloys Stainless Steel India Exporters Stainless Steel 904L Square Pipes

Chemtech Alloys Stainless Steel India Exporters Stainless Steel 904L Rectangular Pipes

STAINLESS STEEL PIPES 904L manufacturer
Chemtech Alloys Stainless Steel India are remarkable Exporters, Suppliers & Stockiest of an extensive scope of Stainless Steel 904L Pipes from Mumbai, India.

UNS NO8904, generally known as 904L stainless steel, is a low carbon austenitic nickel-chromium stainless steel with increments of molybdenum and copper. 904L pipe fittings and 904L product structures are principally utilized where the erosion safe properties of 316L and 317L are deficient, particularly in extreme destructive conditions.

In Most Environments 904L Stainless Steel has an erosion execution middle between the standard & austenitic evaluation 316L and the exceptionally alloyed 6 Mo and comparable super austenitic evaluation.

Albeit initially produced for its imperviousness to sulphuric corrosive it additionally has a high imperviousness to an extensive variety of situations. A PRE of 35 shows that the material has great imperviousness to warm ocean water and other high chloride situations. High nickel substance brings about a vastly improved imperviousness to stretch erosion breaking than the standard austenitic evaluations. Copper adds imperviousness to sulphuric and other decreasing acids, especially in the extremely forceful "mid focus" range.

In many situations SS 904L has a consumption execution middle of the road between the standard austenitic level SS 316L and the much alloyed 6% molybdenum and comparable "super austenitic" levels.

In forceful nitric corrosive SS 904L has less resistance than without molybdenum evaluations, for example, SS 304L and SS 310L.

For greatest anxiety erosion breaking resistance in basic situations the steel ought to be arrangement treated after chilly work.

Good resistance to oxidation, Great imperviousness to oxidation, however like other exceedingly alloyed evaluations experiences structural insecurity (precipitation of fragile stages, for example, sigma) at raised temperatures. 904L ought not to be utilized above around 400°C. Annealing heat to 1090-1175°C and cool rapidly. Susceptible to hot cracking in constrained weld elements. It has high purity, low sulphur grade.

Application :

Condensers, processing plant for sulphuric, phosphoric and acetic acids, Pulp and Paper Industry, Seawater cooling equipment, Chemical equipment

Product specification: :

Range: 15 NB UP TO 200 NB In Seamless
150NB UP to 500NB in welded
Schedule: SCH10/10S, SCH20, SCH30, SCH40/40S, STD, SCH80/80S, XS
Specifications : ASTM B677, B366
ASME SB677, SB366
Type: Seamless / ERW / Welded/ Fabricated

Table 1. Chemical Composition

C Cr Cu Mn Mo Ni P S Si
Max Max Max Max Max
0.02 19.0-23.0 1.0-2.0 2.0 4.0-5.0 23.0-28.0 0.045 0.035 1.0

Table 2. Mechanical Properties(Room Temperature)


Temper Annealed
Tensile Rm 71 ksi (min)
Tensile Rm 490 MPa (min)
R.p. 0.2% Yield 32 ksi (min)
R.p. 0.2% Yield 220 MPa (min)
Elongation (2” or 4D gl) 35 % (min)

Table 3. Physical Properties

Specific Heat (0-100°C) 450 J.kg-1.°K-1
Thermal Conductivity 11.5 W.m -1.°K-1
Thermal Expansion 15.8 mm/m/°C
Modulus Elasticity 190 GPa
Electrical Resistivity 9.52 μohm/cm
Density 7.95 g/cm3